Propertiesof Aluminum Honey-comb Core

Properties	Values
Properties	1/4”	3/8”	1/2”	3/4”
Density(kg/m3)	80	54	38	29
Compression Strength Unstabilized(kg/mm2)	0.46	0.25	0.14	0.09
Compression Strength Stabilized(kg/mm2)	0.48	0.27	0.15	0.095
Compression Module Stabilized(kg/mm2)	108	67	29	17
Crush Strength(kg/mm2)	0.18	0.087	0.044	0.032
Plate Shear Strength/L-Direction(kg/mm2)	0.25	0.16	0.09	0.07
Plate Shear Module/L-Direction(kg/mm2)	0.05	0.03	0.02	0.014
Plate shear Strength/W-Direction(kg/mm2)	0.15	0.03	0.02	0.014
Plate shear Module/L-Direction(kg/mm2)	0.027	0.015	0.009	0.008
Bonding Strength between foil(kg/mm2)	35	27	23	20
Flammability(kg/mm2)	Non-Combustible

Facing Materials	Yield Strength (Kg/cm2)	Modules of Elasticity(Kg/cm2)	λ(1-μ2)
Aluminum A3005 – H16 A5052 – H34	1266 1687	7.⁰³ X 10⁵ 7.¹⁰X10⁵	0.89 0.89
Stainless Steel 304 316	2461 2461	1.⁹⁷X10⁶ 1.⁹⁷X10⁶	0.94 0.94
Pine plywood Lauan plywood Hard wood	211 158 253	1.²⁷X10⁵ 1.²⁷X10⁵ 4.⁵⁶X10⁴	0.99 0.99 0.99

Test Type		TestingConditions			Quality standards		Remarks
					High DurabilityP.E	P.V.D.F
Color		1.By eye 2.Colordifference-meter			O.K within range ΔE = 1.0 or less	O.K within range ΔE = 1.0 or less
Gloss		GLOSS METER(60)		Full light	70% or more	Not Applicable
				Half light	20~70% or less	Not Applicable
				No light	20% or less	30% or less
Pencil Hardness		MITSUBISHI UNI –PENCIL			H or harder	H or harder
Coating Thickness	TOP SIDE	ELCOMETER			25±3㎛	25±3㎛
	BACK SIDE				5±2㎛	5±2㎛
1^st Adherence Test	ERICHSEN	1mm spacingxH100 CROSS-CUTXERICHSEN 6mm			100/100	100/100	Forced/NaturalAbrasion (max score:100)
	IMPACT	C 1/2”X1kgX50cm			No abrasion of thecoat	No abrasion of thecoat
2^ndAdherence Test	ERICHSEN	ERICHSEN 6mm after 1mm spacingxH100CROSS-CUT			100/100	100/100	Forced/NaturalAbrasion (max score:100)
	IMPACT	C 1/2”X1kgX50cm			No abrasion of thecoat	No abrasion of thecoat
MEK Rubbing		Rub twice with MEKSoaked piece of cloth			30 times or more	30 times or more
Heat Resistance		170℃x1hour			ΔE = 1.5 or less	ΔE = 1.5 or less
Bending		25±5℃x180˚BENDING			6T NO CRACK	5T NO CRACK
Stain Resistance	Monamioil Magicink #300	BLACK	Removed with acetone after piece 24hours exposure(20±2℃)		Easily removable with no traces.	Easily removablewith no traces
		BLUE
		RED
	LIPSTIC
Chemical Resistance	5% CH3COO	Washing and Dryingafter 20±2℃ X Spot Test			No changes to coat	No changes to coat	P/E:24hour High DurabilityP.E:48hour P.V.D.F.:72hour
	5%HCL
	5%NAOH
	TOLUENE
	XYLENE
Corrosion Rosistance (Salt spray)		35±2℃2x5%Nacl Continuous Spray(Edge sealed)			No blister at 2mm Or deeper from the Cross cut	No blister at 2mm Or deeper from the Cross cut	P/E:500hour High DurabilityP.E:1000hour P.V.D.F:1000hour
Weather Resistance (Q-UV Test)		DEW CYCLE (1CYCLE) (UV-test(60℃)4hour+(50℃)4hour condensation)x3			ΔE = 3.0 or less (white color)	ΔE = 5.0 or less (white color)	P/E:500hour High DurabilityP.E:1000hour P.V.D.F:5000hour
Base Metal		-			AL	AL
Usage		-			Constructionmaterial	Constructionmaterial	-

PROJECT FOCUS


Building	CSC Building Talavera Rd North Ryde
Architect	James Fitzpatrick of Fitzpatrick & Partners
Product	Alpolic
The visual aims of the project required a flexible panelised cladding system available in a range of bright yet fade resistant colours. The versatility and aesthetic quality of the product along with the confidence of being supported by Mitsubishi Chemical meant that Alpolic was the choice.